Specifications:AMS 5544, AMS 5706, AMS 5707, AMS 5708, AMS 5828
Waspaloy® Wire Description
Waspaloy® is an age hardenable nickel-base alloy with excellent high temperature strength and good resistance to oxidation at temperatures up to 1600°F. The alloy’s high-temperature strength isderived from its solid solution strengthening elements,molybdenum, cobalt and chromium, and its agehardening elements of aluminum and titanium. Waspaloy® has higher stability and strength ranges than those available for alloy 718. Itcan be heat treated in three-steps: solution treatment, stabilization and age-hardening
Gas turbine seals
Iron: 3.00 max
Manganese: 0.10 max
Silicon: 0.15 max
Phosphorus: 0.015 max
Sulfur: 0.015 max
Density, 0.296 lbs/in³, 8.20 g/cm³
Mean Coefficient of Thermal Expansion: µin/in-°F (µm/m-°C): 70-800°F (20-500°C): 7.6 (13.9)
70-1000°F (20-600°C): 7.8(14.3)
70-1200°F (20-700°C): 8.1(14.8)
70-1400°F (20-800°C): 8.4(15.4)
70-1600°F (20-900°C): 8.9(16.4)
70-1800°F (20-1000°C): 9.7(17.8)
Thermal Conductivity: BTU-in/ft-°F (W/m-°K):
At 70°F (21°C): 79(11)
At 800°F (427°C): 113(16)
At 1200°F (649°C): 138(20)
At 1500°F (816°C): 160(23)
At 1800°F (982°C): 182(26)
Modulus of Elasticity, KSI(MPa)
30.9 x 10³(213 x 10³) in tension
Melting Range: 2425-2475°F (1330-1357°C)
Mechanical Properties at Room Temperature
Mechanical properties are size and process dependent. Contact Ulbrich Wire with requests.
Mechanical properties are size and process dependent. Contact Ulbrich Wire with requests
Heat Treated Capabilities:
Heat treated properties are size and process dependent. Contact Ulbrich Wire with requests
Refer to NACE (National Association of Corrosion Engineers) for recommendations
Standard Wire Finishes
Extra Clean: (XC) Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
Waspaloy® can be cold-formed in the annealed condition, and may also be hot-formed at temperatures of 1900°F or above.
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”
*Waspaloy® is a registered trademark of United Technologies Corp
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.