FLAT, SHAPED & ROUND WIRE
ASTM B 152, ASTM B747, QQ-C-576
Applications
Electrical/electronic and solar applications where strength is not required. Additional applications are downspouts, gutters, roofing, gaskets, heat sinks, busbars, nails, printing rolls, rivets, etc. parts.
Description
In general, copper alloys exhibit good to excellent corrosion resistance and high thermal conductivity and very high electrical conductivity. Pure copper’s electrical conductivity is so high that many metals are measured against it in the form of the IACS (International Annealed Copper Standard).
Chemistry Typical¹‚²
| UNS # | Copper 3 | Oxygen | Silver | Phosphorus | Arsenic |
|---|---|---|---|---|---|
| C10100 | 99.99 min | 0.0005 max | 0.0005 max | ||
| C10200 | 99.95 min | 0.001 max | 0.0003 max | ||
| C10400 | 99.95 min | 0.001 max | 0.027 min | ||
| C10500 | 99.95 min | 0.001 max | 0.034 min | ||
| C10700 | 99.95 min | 0.001 max | 0.085 min | ||
| C11000 | 99.90 min | ||||
| C12000 | 99.90 min | 0.004-0.012 | |||
| C12100 | 99.90 min | 0.014 | 0.004-0.012 | ||
| C15000 | Balance 4 | 0.10-0.20 Zr | |||
| C15500 | 99.75 min | 0.027-0.10 | 0.040-0.080 | 0.08-0.13 Mg |
1. Contact Ulbrich Wire for request regarding the availability of other copper alloys
2. Contact Ulbrich Technical Department for limits for additional trace elements and impurity levels
3. Copper Values include Silver
4. Copper plus named elements
Physical Properties
Typical Density: 0.332 lb/in3, 8.92 g/cm³
Electrical Conductivity: (% IACS at 68°F 20°C, annealed): 85-101%
Specific Heat: BTU/lb-°F (J/g-°C): 0.0920 (0.385)
Thermal Conductivity: BTU-in/hr-ft2-°F (W/m•K): 2712 (390.8)
Mean Coefficient of Thermal Expansion:µin/in-°F(µm/m-°C)
68 – 572 °F (20 – 300 °C): 9.8 (17.6)
Modulus of Elasticity: KSI (MPa)
17 x 10³( x 10³) in tension
Melting Range: 1981°F (1083°C):
Forms
Profile, Round, Flat, Square
Mechanical Properties at Room Temperature
Properties: Annealed Typical
Ultimate Tensile Strength: 26-38 KSI (179-262 MPa)
Yield Strength: 10 KSI (69 MPa) Nominal
Elongation: 35%
Properties: Tempered
Copper alloys can be cold worked to various tempers.
5. Actual physical and mechanical properties are alloy dependent. Contact Ulbrich Technical Service for alloy specific properties
Additional Properties
Corrosion Resistance
Contact Ulbrich Wire for specific information
Wire Finishes
XC-Extra clean. Annealed or annealed and cold rolled
∗Contact Ulbrich Wire with special finish requests
Heat Treatment
Copper alloys are non hardenable by heat treatment.
Welding
Contact Ulbrich Wire for specific information
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.