Shaped, Flat, Square, Round, Fine Wire, Plated and Bare Wire
AMS 5640, AMS 5641, ASTM A582, QQ-S-764
303se Alloy Description
Alloy 303Se alloy is a free-machining stainless steel specifically designed to exhibit improved machinability. It is a non-magnetic austenitic stainless steel which is not hardenable by heat treatment. Selenium replaces sulfur to produce the free-machining characteristics and has somewhat improved formability over 303. The good mechanical and corrosion-resistant properties of the lower-sulfur grade are retained to the extent possible.
Intricate parts that can only be made by machining.
Carbon: 0.12 max
Manganese: 2.00 max
Density: 0.283 lb/in³, 8.00 g/cm³
Electrical Resistivity: ohm-cir-mil/ft:
At 70°F: 433.0
Specific Heat: BTU/lb-°F (J/g-°C) 32-212°F (0-100°C): 0.12(0.5)
Thermal Conductivity: BTU-in/hr-ft²-°F (W/m•K)
At 212 °F (100°C): 112 (16.20)
Mean Coefficient of Thermal Expansion: µin/in-°F (µm/m-°C)
68 – 392 °F (20 – 200 °C): 9.3 (16.7)
Modulus of Elasticity: ksi (MPa)
28 x 10³ Ksi (193 x 10³) in tension
Melting Range: °F (°C): 2550-2590 (1400-1420)
Mechanical Properties at Room Temperature
Properties: Annealed Typical
Ultimate Tensile Strength: 75 KSI min (517 MPa min)
Yield Strength: 25 KSI min (172 MPa min)
Elongation: 35 % min
303Se can be cold worked to various tempers. Contact Ulbrich Shaped Wire Technical Service for additional information
Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Standard Wire Finishes
Extra Clean: (XC) Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process andis not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
• Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
303Se is non hardenable by heat treatment.
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”.
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.
Copyright© January 2014 Ulbrich Stainless Steels & Special Metals, Inc. – Revision 6.1.2015