Shaped, Flat, Square, Round, Fine Wire, Plated and Un-plated
ASTM A167, ASTM A240
317L Alloy Description
Alloy 317L is a low carbon variation of alloy 317. This austenitic chromium-nickel stainless steel can be used in applications where it is not possible to anneal after welding and where maximum corrosion resistance is required. It provides good oxidation resistance in intermittent service to 1600°F and in continuous service to 1700°F.
Screens for marine and chemical applications
Pulp and paper applications
Seals and other components for the oil and gas industry
Carbon: 0.030 max
Manganese: 2.00 max
Silicon: 0.75 max
Phosphorus: 0.045 max
Density 0.29 lbs/in³, 7.99 g/cm³
Electrical Resistivity, microhm-in (microhm-cm):
68°F (20°C): 31.19 (79.0)
Specific Heat: BTU/lb/°F (kJ/kg•K):
32-212°F (0-100°C): 0.12 (0.50)
Thermal Conductivity: BTU/hr/ft²/ft/°F (W/m•K)
At 212°F (100°C): 9.4 (16.2)
At 932°F (500C): 12.4 (21.4)
Mean Coefficient of Thermal Expansion:in/in/°F (μm/m•K)
32-212°F (0-100°C): 8.9 x 10-6(16.0)
32-600°F (0-315°C): 9.0 x 10-6(16.2)
32-1000°F (0-538°C): 9.7 x 10-6(18.5)
32-1500ºF (0-871ºC): 11.1 x 10-6(18.5)
Modulus of Elasticity: KSI (MPa)
28.0 x 10³ (193 x 10³) in tension
11.2 x 10³ (77 x 10³) in torsion
Magnetic Permeability: H = 200 Oersteds: Annealed:< 1.02 max.
Melting Range: °F (°C) 2500 – 2590 (1371 – 1421)
Mechanical Properties at Room Temperature
Ultimate Tensile Strength: 75 KSI min (515 MPa min)
Yield Strength: (0.2% Offset) 30 KSI min (205 MPa min)
Elongation: 35% min
Hardness: Rb 95 max
Alloy can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
See NACE (National Association of Corrosion Engineers) for recommendations.
Standard Wire Finishes
Extra Clean: (XC) Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
Alloy 317L can be readily formed and drawn.
Alloy 317L is non hardenable by heat treatment and can only be hardened by cold working.
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”.
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.
Copyright© January 2014 Ulbrich Stainless Steels & Special Metals, Inc. – Revision 6.1.2015