Square, Round, Fine Wire, Plated and Un-plated (Rectangular cross sections: Inquiry with Ulbrich Shaped Wire Sales)
ASTM A484, ASTM A 582, AMS 5610, QQ-S-764, Mil-W-5263
Alloy 416 is a free machining martensitic grade of stainless. Parts can be fabricated in the soft condition then hardened by heat treating to increase strength and hardness. The addition of sulfur increases the machinability over austenitic grades but alloy 416 sacrifices corrosion resistance.
Any part that requires considerable machining
Carbon: 0.15 max
Phosphorus: 0.060 max
Silicon: 1.00 max
Manganese: 1.25 max
Sulfur: 0.150 min
Density: .282 lb/in³, 7.80 g/cm³
Electrical Resistivity: ohm-cir-mil/ft:
At 70 °F (21°C): 343.0
Specific Heat: BTU/lb-°F (J/g-°C):
32-212°F (0-100°C): 0.110 (0.460)
Thermal Conductivity: BTU-in//hr-ft²-°F (W/m•K)
At 200 °F (94 °C): 172.8 (24.9)
At 1000 °F (538 °C): 198 (28.5)
Mean Coefficient of Thermal Expansion: µin/in-°F (µm/m-°C)
32-212 °F (0-100 °C): 5.50 (9.90)
32-600 °F (0-316 °C): 5.60 (10.1)
32-1200 °F (0-649 °C): 6.5 (11.7)
Modulus of Elasticity: KSI (MPa)
29.0 x 10³ (200 x 10³) in tension
Melting Range: °F (°C): 2700-2790 (1488-1530)
Mechanical Properties at Room Temperature
Properties: Annealed Typical
Ultimate Tensile Strength: 75 KSI min (517 MPa min)
Yield Strength: 40 KSI min (276 MPa min)
Elongation: 30 % min
Alloy 416 can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Standard Wire Finishes
Extra Clean: (XC) Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
Alloy 416 can be hardened by cold working and by heat treatment.
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”.
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.