Shaped, Flat, Square, Round, Fine Wire, Plated and Bare Wire
AMS 5503, AMS 5627, ASTM A-240, ASTM A-479, ASTM A-493, ASTM 580
Alloy 430Li is a low interstitial ferritic stainless steel similar to alloy 430. It is non-hardenable by heat treatment, magnetic and can be readily drawn and formed. Its drawing characteristics are similar to those of low carbon steel, although it is stronger in the annealed condition and will require stronger tooling and increased power. It is also adaptable to most hot-forming operations.
Interior architectural screens
Interior trim applications
Carbon: 0.12 max
Manganese: 1.00 max
Silicon: 1.00 max
Chromium: 16.00 – 18.00
Nickel: 0.50 max
Molybdenum: 0.50 max
Phosphorus: 0.040 max
Sulfur: 0.030 max
Copper: 0.50 max
Density, 0.280lbs/in³, 7.74 g/cm³
Electrical Resistivity, microhm-in (microhm-cm):
68°F (20°C): 23.68 (60)
Specific Heat, BTU/lb/°F (kJ/kg•K):
32-212°F (0-100°C): 0.11 (0.46)
Thermal Conductivity, BTU/hr/ft2/ft/°F (W/m•K):
At 212°F (100°C): 15.1 (26.1)
At 932°F (500°C): 15.2 (26.3)
Mean Coefficient of Thermal Expansion, in/in/°F (μm/m•K):
32-212°F (0-100°C): 5.8 x 10-6(10.4)
32-1000°F (0-538°C): 6.3 x 10-6(11.4)
Modulus of Elasticity, KSI (MPa)
29.0 x 10³ (200 x 10³) in tension
Magnetic Permeability: Magnetic
Melting Range, °F (°C) 2600-2750 (1427-1510)
Mechanical Properties at Room Temperature
Ultimate Tensile Strength: 65 KSI min (450 MPa min)
Yield Strength (0.2% offset): 30 KSI min (205 MPa min)
Elongation: 22% min
Hardness: Rb 89 max
Alloy 430Li can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
Refer to NACE (National Association of Corrosion Engineers) for recommendations
Standard Wire Finishes
Extra Clean: Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
Alloy 430Li it is non-hardenable by heat treatment.
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.