Duplex Alloys 2205 Alloy Description
Duplex 2205 is a two-phase ferritic/austenitic. It is the most widely used duplex stainless steel grade and is characterized by high yield strength, double that of the standard austenitic stainless steel grades. It demonstrates good fatigue strength, as well as outstanding resistance to stress-corrosion cracking, crevice, pitting, erosion and general corrosion in severe environments.
Screens and other components for the pulp and paper industry
Well screens for oil and gas industry
Components for the chemical processing industry
Carbon: 0.30 max
Silicon: 1.0 max
Manganese: 2.00 max
Phosphorus: 0.03 max
Sulfur: 0.020 max
Density: 0.285 lbs/in³, 7.88 g/cm³
Thermal Conductivity: BTU-ft/hr/ft² °F (W/m-°K)
68-212ºF (20-100ºC): 11.0 (19.0)
Mean Coefficient of Thermal Expansion: in/in/°F (μm/m•K)
32-212°F: 7.6 x 10-6(13.7)
Modulus of Elasticity: KSI (MPa)
27.5x 10³ (190 x 10³) in tension
Mechanical Properties at Room Temperature
Ultimate Tensile Strength: 90 KSI min (620 MPa min)
Yield Strength: (0.2% offset): 65 KSI min (448 MPa min)
Elongation: 25% min
Hardness: Rc 32 max
Duplex 2205 can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
Refer to NACE (National Association of Corrosion Engineers) for recommendations
Standard Wire Finishes
Extra Clean: Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
Duplex 2205 cannot be hardened by heat treatment
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.