Inconel® 600 (Alloy 600), Description
Inconel®Alloy 600 is a nickel-chromium alloy with excellent carburization and good oxidation resistance. It was designed for use from cryogenic to elevated temperatures in the range of 2000°F (1093°C). The high nickel content of the material provides exceptional resistance to chloride stress corrosion cracking.
Applications
Furnace components
Chemical and food processing applications
Flexible metal hose
Chemistry Typical
Nickel + Cobalt: 72.0 min.
Chromium: 14.0-17.0
Iron: 6.00-10.00
Carbon: 0.15 max.
Manganese: 1.00 max
Sulfur: 0.015 max.
Silicon: 0.50 max.
Copper: 0.50 max
Physical Properties
Density: 0.304 lbs/in³, 8.42 g/cm³
Electrical Resistivity, ohm-circ mil/ft, (μΩ-m):
620 (1.03)
Specific Heat, Btu/lb-°F, (J/kg-°C):
0.106 (444)
Mean Coefficient of Thermal Expansion: in/in/°F (mm/m/°C)
70-200°F (21-93°C)– 6.9 x 10-6(12.4)
70-400°F (21-204°C)- 7.3 x 10-6 (13.1)
Modulus of Elasticity: KSI (MPa)
30 x 10³ (207 x 10³) in tension
Melting Range: 2470-2576°F (1354-1413°C)
Magnetic Permeability, H = 200 Oersteds: Annealed: 1.010
Mechanical Properties at Room Temperature
Annealed
Ultimate Tensile Strength: 80 KSI min (552 MPa min)
Yield Strength: (0.2% offset) 35 KSI min (241 a min)
Elongation: 30% min: gauges > 0.010 inches
Properties: Tempered
Alloy 600 can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
Tempered: Hard
Ultimate Tensile Strength: 125 KSI min (860 MPa min)
Yield Strength: (0.2% offset) 90 KSI min (620 MPa min)
Elongation: 2% min ( gauges > 0.010 inches)
Hardness: Rc 30 min
Additional Properties
Corrosion Resistance
Refer to NACE (National Association for Corrosion Engineers) for recommendations
Standard Wire Finishes
Extra Clean: (XC) Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Forms
Continuous Coils
Cut to lengths
Precision cutting
Heat Treatment
Alloy 600cannot be hardened heat treating
Welding
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”
*Inconel® 600 is a registered trademark of Special Metals Corp
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.
Copyright© January 2014 Ulbrich Stainless Steels & Special Metals, Inc. – Revision 6.1.2015