Shaped, Flat, Square, Round, Fine Wire, Plated and Bare Wire
ASTM B 160, ASTM B162, AMS 5553
Nickel 200 Description
Nickel is a wrought commercially pure Nickel with a maximum carbon level of 0.15%. This alloy provides highly ductile mechanical properties across a wide temperature range. It provides corrosion resistance in neutral to moderately reducing environments, provides high thermal and electrical conductivity in comparison to nickel-base alloys, stainless and low alloy steels. This alloy is not recommended for service above 600°F (316°C) because long-time exposures in the 800°F to 1200°F range result in precipitation of a carbon containing phase and loss of ductility.
Electronic components where going maybe required
Bands and tags
Nickel + Cobalt: 99.00 min
Carbon: 0.15 max
Manganese: 0.35 max
Silicon: 0.35 max
Sulfur: 0.010 max
Iron: 0. 40 max
Copper: 0.25 max
Density, 0.321 lbs/in³, 8.89 g/cm³
Specific Heat: BTU/lb/°F (J/kg•K):
32-212°F (0-100°C): 0.12 (456)
Thermal Conductivity, BTU/hr/ft²/ft/°F (W/m•K)
At 212ºF (100ºC): 38.8(67.1)
At 400°F (204°C): 35.4(61.3)
At 600ºF (316ºC): 36.5(56.3)
Mean Coefficient of Thermal Expansion: in/in/°F (μm/m•K)
80-200°F (27- 93°C): 7.4 x 10-6(13.3)
80-400°F (27-204°C): 7.7x 10-6(13.9)
80-600°F (27-316°C): 8.0x 10-6(14.4)
Modulus of Elasticity, KSI (MPa)
30.0x 10³ (207 x 10³)
Melting Range: 2615-2535°F (1435-1445°C)
Mechanical Properties at Room Temperature
Ultimate Tensile Strength: 55 KSI min (380 MPa min)
Yield Strength (0.2% offset): 15 KSI min (100 MPa min)
35% min: gauges ≤ 0.0035 inches
40% min: gauges > 0.0035 inches
HV 117 max: gauges ≤ 0.010 inches
Rb 66 max: gauges > 0.010 inches
Nickel 200 can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Standard Wire Finishes
Extra Clean: Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
Nickel 200 is non hardenable by heat treatment.
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.