Ultimet® Alloy Description
ULTIMET® is a cobalt-based alloy with excellent resistance to galling, cavitation erosion, slurry erosion, liquid droplet impact. Ideal welding material with exceptional ductility and resistance to weld cracking, very easy to apply as an overlay, multiple layers applicable with little to no preheat.
Bolts and screws
Chromium: 26 nominal
Nickel: 9 nominal
Molybdenum: 5 nominal
Tungsten: 2 nominal
Manganese: 0.8 nominal
Silicon: 0.3 nominal
Nitrogen: 0.08 nominal
Carbon: 0.06 nominal
Density: 0.306 lb/in³, 8.47 g/cm³
Electrical Resistivity: µohm-in (µohm-m)
At 73°F (23°C): 34.2 (0.87)
At 212°F (100°C): 35.4 (0.89)
At 392°F (200°C): 36.6 (0.93)
At 572°F (300°C): 38.1 (0.96)
At 752°F (400°C): 39.3 (1.00)
At 932°F (500°C): 40.5 (1.03)
At 1112°F (600°C): 41.3 (1.05)
Specific Heat: BTU/lb-°F (J/Kg-K):
At 73°F (23°C): 0.109 (456)
At 212°F (100°C): 0.112 (470)
At 392°F (200°C): 0.115 (482)
At 572°F (300°C): 0.121 (504)
At 752°F (400°C): 0.126 (525)
At 932°F (500°C): 0.130 (545)
At 1112°F (600°C): 0.137 (573)
Thermal Conductivity: BTU-in/hr-ft²-°F (W/m•K)
At 73°F (23°C): 85 (12.3)
At 212°F (100°C): 96 (13.8)
At 392°F (200°C): 108 (15.6)
At 572°F (300°C): 121 (17.5)
At 752°F (400°C): 134 (19.4)
At 932°F (500°C): 149 (21.5)
At 1112°F (600°C): 166 (23.9)
Mean Coefficient of Thermal Expansion: µin/in-°F (m/m-K)):
78-200°F (26-93°C): 7.2 (13.0 x 10-6)
78-400°F (26-204°C): 7.5 (13.5 x 10-6)
78-600°F (26-316°C): 7.8 (14.0 x 10-6)
78-800°F (26-427°C): 8.0 (14.5 x 10-6)
78-1000°F (26-538°C): 8.2 (14.8 x 10-6)
78-1200°F (26-649°C): 8.4 (15.1 x 10-6)
78-1400°F (26-760°C): 8.8 (15.9 x 10-6)
78-1600°F (26-871°C): 9.1 (16.4 x 10-6)
78-1800°F (26-982°C): 9.4 (16.9 x 10-6)
Modulus of Elasticity:KSI (MPa)
31.2 x 10³ (215 x 10³) in tension
Melting Range: 2430-2470°F (1332-1354°C)
Properties: Annealed Typical
Ultimate Tensile Strength: 138 KSI min (951 MPa min)
Yield Strength: 72 KSI min (496 MPa min )
Elongation: 42% min
ULTIMET® can be cold rolled to achieve the temper properties required by specific customers and/or manufacturing requirements. Contact Ulbrich Wire for details.
Refer to NACE (National Association of Corrosion Engineers) for recommendations.
Standard Wire Finishes
Extra Clean: (XC) Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”
Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for decorative applications
Soap (round wire only): Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.
Plated: Many plating options are available.
∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.
Cut to lengths
ULTIMET® is hardenable by cold working. Inquire with Ulbrich Technical Service for heat treat responses.
For best results refer to: SSINA’s “Welding of Stainless Steels and Other Joining Methods”.
*ULTIMET® is a registered trademark of Haynes International Corp.
Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels and Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the ‘applications’ noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.